車軸中心部合金超弾性合金素材 3J40
PrecisionAlloy3J40
ショック-proofandamp;WearResistantaxle-centrealloy(YB/T5243-1993)
使用法: Itisappliedtoproducetheaxle-centreofinstrumentandmeteraswellastheaxle-centreofthestaff
GradeandChemicalComposition(seeTable1)
Table1GradeandChemicalComposition
グレード |
ChemicalComposition(%) |
|||||||||
C |
P |
S |
Mn |
Si |
Fe |
Cr |
A1 |
Ce |
Ni |
|
≤ | ||||||||||
3J40 |
0.03 |
0.010 |
0.010 |
0.10 |
0.20 |
0.50 |
39.0~41.0 |
3.30~3.50 |
0.10~0.2 |
バランス |
© Basedonaddition
MechanicalProperty(seeTable2)
Table2MechanicalProperty
像 |
VickersHardness ・ HV |
CommendedHeat 治療 |
BendTestTheradiusof themandrelis twiceasthediameter ofthealloy |
|||
私 |
Ⅱ |
Ⅲ |
||||
ColdDrawing |
450~510 |
Bend90degrees。 Nocracksandbroken ontheoutsideofthebending |
||||
ColdDrawnandamp;高齢化 |
780~830 |
andgt; 830 〜 880 |
andgt; 880 |
480 ~ 540 ° C Keepwarmfor5h |
Note:1.Thedefaulthardnessclassificationofthealloywireincolddrawingandamp; agingstatusisclassII。
PhysicalProperty(seeTable3—Table5)
Table3CoefficientofLinearExpansion
状態 |
||||||
20 〜 55 ° C |
20 ~ 100 ° C |
20 〜 200 ° C |
20 ~ 300 ° C |
20 ~ 400 ° C |
20 ~ 500 ° C |
|
固溶 |
12.2~12.7 |
12.4~12.5 |
12.6~12.8 |
13.0~13.1 |
13.5~13.6 |
13.8~14.0 |
SolidSolutionandamp; 高齢化 |
11.0~11.5 |
11.9~12.0 |
12.0~12.2 |
12.4~12.5 |
12.7~12.8 |
13.1~13.3 |
ColdDrawnandamp; 高齢化 |
11.6 |
12.0 |
12.1 |
12.4 |
12.8 |
13.3 |
Table4ModulusofElasticityandamp;FrequencyTemperatureCoefficient
状態 |
ModulusofElasticity |
MechanicalQuality FactorQ20 ° C |
||
20 ~-40 ° C |
20 ~ 100 ° C |
|||
固溶 + 80% 入れなければ |
176500~196000 |
|||
固溶 + 80% 入れなければ + Aging5h |
225500~235500 |
-103~-106 |
-104~-110 |
49000~51000 |
Table5MagneticSusceptibilityandamp;比抵抗
状態 |
MagneticSusceptibility |
Resistivity/(μΩ•m) |
Density/(g/cm³) |
|
H = 40KA/m |
H:80KA/m |
|||
固溶 |
3.5~4.5 |
3.5~4.6 |
7.6 |
|
固溶 + 高齢化 |
3.8~4.0 |
2.4~4.2 |
||
固溶 + ColdDrawing |
2.8~3.0 |
1.21 |
||
固溶 + 69% 入れなければ + 高齢化 |
0.78 |
CorrosionResistingProperty(SeeTable5)
Table5CorrosionResistingProperty
状態 |
SaltFogTest |
LongtimeStore inTheAir |
ColdDrawing + 固溶 + 高齢化 |
Nocorrosionafter240hours(TestedbythebuyerperJB1606) |
Nocorrosion |